Raw material preparation: The raw materials required to make Moissanite are high-purity carbon and silicon. Metallurgical grade carbon powder and high purity silica are typically used as starting materials.
Carbonization reaction: Put carbon powder and silica into a high-temperature furnace and perform carbonization reaction under vacuum or inert atmosphere. At high temperatures (approximately 2000°C), carbon and silicon react to form silicon carbide.
Crystal growth: By controlling temperature and pressure conditions, silicon carbide grows in the form of crystals. The high-temperature and high-pressure method is usually used, in which silicon carbide is placed in a high-temperature and high-pressure device to allow it to grow gradually over a period of days to weeks.
Cutting and Polishing: Grown Moissanite crystals need to be cut and polished to obtain the desired shape and luster. The process is similar to working on natural diamonds.
The growth process of Moissanite requires a simulated high-temperature and high-pressure environment to promote the growth of silicon carbide crystals. By controlling parameters such as temperature, pressure and time, the size and quality of Moissanite crystals can be adjusted.
Moissanite has some characteristics compared with natural diamonds:
Appearance: Moissanite has a diamond-like appearance with a sparkling fire effect. It usually appears colorless or white, but other colors can occur.
Optical properties: Moissanite has a high refractive index and dispersion rate, which gives it a strong sparkling effect when illuminated by light. It also scatters light, creating iridescent fire.
Hardness: Moissanite has a very high hardness, second only to diamond. It has a hardness of approximately 9.25 on the Mohs scale, compared to 10 for diamond.
Price: Compared with natural diamonds, Moissanite has a lower price and is an economical choice. It can provide similar appearance and performance as diamond, but at a more affordable price.
It should be noted that Moissanite is a man-made gemstone that, although similar in appearance and performance to diamonds, is not naturally formed. It is widely used in the jewelry industry as a substitute for diamonds.
And I love it!! I highly recommend Mathew from Fiorese. The process was a breeze, manufacturing took less than week...
Received my 3.29ct OMC from Sonia at Fiorese. She was a pleasure to deal with and was very patient with...
First time with Melody at Fiorese. She was so awesome to work with. 8.5mm OEC moissanite in 10k white gold....